Excellent adhesion with zinc material, aluminum materialm stainless steel etc. nonferrous metal.
Mainly used for zincification material, aluminum material, copper material etc. nonferrous metal substrate, as a use of linking paints.
|
Substrate treatment:
|
Remove surface oil stain, dustzinc salt of the zinc material etc. nonferrous metal.
|
|
Matching:
|
Applicable substrate:
Zinc materiala, luminum material, stainless steel etc. nonferrous metal.
Applicable upper coatings:
Compatible with all intermediate paints, finishes
|
|
Technical constants
|
Drying time and&Coating interval
|
|
Mixing ratio: Host crystal/Firming agent=8/1(by weight)
Standard film thickness:
Dry: 30μm/coat
Academic spreading rate:
0.09kg/ m2/30μm
Solid contents: 71.3%
Humidity requirement: below 85%
|
Temperature(℃): 10 20 30
Dry to touch( hrs): 2 1.5 1
Dry semi-hard( hrs): 14 10 8
Min. interval( hrs): 14 10 8
|